  • Good Price Boiler Plate
  • Good Price Boiler Plate

Good Price Boiler Plate

  • Grade: P265GH,P295GH,16Mo3,13CrMo4-5,10CrMo9-10
Interested in this Ad? Contact the Seller!
toux Janet Chang

+86-185 1669 6028

Click To Email Seller

  

Share this ad

Pinterest Email LinkedIn Google+ Facebook Twitter Addthis

Specification, Chemical & Mechanical Performance

Mainly supplied in forms of coil, sheet, plate, rod, bar, tube, pipe, beam, angle, flange, wire, strip, channel, etc., with various varieties, wide range of dimensions, high purity, stable chemical composition, high dimensional accuracy and excellent surface quality, the products are mainly used in the fields of industries such as automobile engineering, railway transportation, aviation, aerospace, machinery, petrochemical, energy, environmental protection,offshore, chemical, oil & gas, military, power plant, nuclear power, pressure vessel, boiler equipment, mold manufacture,etc..

  • Boiler and pressure vessel steel
  • Pipeline steel
  • Bridge steel
  • Nuclear power steelStructural steel
  • Die steel
  • High strength steel
  • Abrasion resistant steel
  • Weathering, corrosion resistant and fire resistant steel
  • High rise building steel
  • Shipbuilding and offshore engineering steel

 

Boiler Steel plates

 MATERIAL DIMENSIONS

Marking

 Material Number

Dimensions[mm]

Non-standard Thicknesses

Thickness

Width

Length

P 265 GH

1.0425

3-250

1000-4000

14000

P 265 GH: 7,9,11,13,

14,17,26,28,32,42,

52,75,85,95,125

P 295 GH

1.0481

5-120

1000-3500

12000

16 Mo 3

1.5415

1,5-200

1000-3000

12000

13 Cr Mo 4-5

1.7335

3-160

1000-3000

12000

P 295 GH: 13,14,18,

26,28

10 Cr Mo 9-10

1.7380

3-120

1000-2500

12000

 Impact energy substantiated in inspection certificates

 Tensile test at emperature of +300℃ conducted for each cast

 

 CHEMICAL COMPOSITION

Marking

Material Number

Type Division1]

Content of Elements 2]- Mass [max%]

C

Si

max

Mn

P

max

S

max

Al

In all

P 265 GH

1.0425

UQ

max0.20

0.400

0.50-1.40

0.030

0.025

min.0.020

P 295 GH

1.0481

UQ

0.08-0.20

0.400

0.90-1.50

0.030

0.025

min.0.020

16 Mo 3

1.5415

LE

0.12-0.20

0.350

0.40-0.90

0.030

0.025

4]

13 Cr Mo 4-5

1.7335

LE

0.08-0.18

0.350

0.40-1.00

0.030

0.025

4]

10 Cr Mo 9-10

1.7380

LE

0.086]-0.147]

0.500

0.40-0.80

0.030

0.025

4]

 

Marking

Content of Elements 2]- Mass [max%]

Cr

Cu

max.3]

Mo

Nb

max

Ni

max

Ti

max

V

max

Cr+Cu+Mo+Ni

max

P 265 GH

max 0.30

0.300

max 0.08

0.010

0.300

0.300

0.020

0.700

P 295 GH

max 0.30

0.300

max 0.08

0.010

0.300

0.300

0.020

0.700

16 Mo 3

max 0.30

0.300

0.25-0.35

-

0.300

-

-

-

13 Cr Mo 4-5

0.70-1.15 3]

0.300

0.40-0.60

-

-

-

-

max 0.50

10 Cr Mo 9-10

2.00-2.50

0.300

0.90-1.10

-

-

-

-

-

1] – non-alloy quality steel, LE=alloy quality steel

2] - Elements not shown in this table must not be intentionally added to steel without the consent of the customer, 

with the exception of those necessary for the manufacturing process. It is necessary to conduct all relevant measures

 in order to prevent transfer of metal elements from metal waste or other materials used in manufacture which have a

 negative impact on the mechanical properties and usability of the steel.

3] - Upon ordering a lower content of Cu and higher admissible content of Sn may be agreed upon e.g. with regard to malleability.

4] - Stipulate content of Al in cast and state in certification.

5] - Should resistance to compressed hydrogen be important, a minimum content of Cr 0.80% may be agreed upon ordering.

6] - For thicknesses of products less than 10 mm a minimum content of C 0.06% may be agreed upon ordering.

7] - For thicknesses of products over 150 mm a maximum content of C 0.17% may be agreed upon ordering.

 

 MECHANICAL PROPERTIES

Marking

W.Nr.

Material Number

Thermal

Processing1]

Nomal Thickness(mm)

Min. yield strength

ReH[MPa]

Tensile strength Rm

[MPa]

Ductility

A[%]

Impact Energy

KV

Testing 

Temperarure

[℃]

Median value

 from 3test [J] min.

P 265 GH

1.0425

N

 

16

265

410-530

23

0

27

16

40

255

40

60

245

60

100

215

22

100

150

200

400-530

150

 

2]

2]

2]

2]

P 295 GH

1.0481

N

 

16

295

460-580

22

0

27

16

40

290

40

60

285

60

100

260

21

100

150

235

440-570

150

 

2]

2]

2]

2]

16 Mo 3

1.5415

N 3]

 

16

275

440-590

24

+20

31

16

40

270

40

60

260

23

60

100

240

430-580

22

27

100

150

220

420-570

19

150

 

2]

2]

2]

2]

13 Cr Mo 4-5

1.7335

N+T

 

16

300

450-600

20

+20

31

16

60

295

N+T

QA

QL

60

100

275

440-590

19

27

QL

100

150

255

430-580

150

 

2]

2]

2]

2]

10 Cr Mo 9-10

1.7380

N+T

 

16

310

480-630

18

+20

31

16

40

300

40

60

290

N+T

QA

QL

60

100

270

470-620

17

27

QL

100

150

250

460-610

150

 

2]

2]

2]

2]

1) N – normalising, QA – hardened in atmosphere, QL – hardened in liquid medium,

    T – tempered, chemical values and 0.2% yield strength at increased temperature, see EN 10028.

2) According to negotiation

3) May be delivered in N + T state in accordance with choice of manufacturer

 

return