فولاد ضد زنگ 303 1.4305

ما می توانیم تولید کنیم 303 1.4305 Stainless Steel stainless steel round rods, 303 1.4305 Stainless Steel forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong Group production experience, strict control 303 1.4305 Stainless Steel chemical composition and 303 1.4305 Stainless Steel mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

فولاد نوار گرد: 1mm به 3500mm

فولاد به شکل مربع: 1mm به 4000mm

Plate steel:0.1mm to 4000mm

عرض: 10mm به 2500mm

دهم: ما می توانیم هر لنج را براساس نیاز مشتری تهیه کنیم.

آهنگری: شفت هایی با پهلوها / لوله ها / لوله ها / شلخته ها / دونات ها / مکعب ها / شکل های دیگر

لوله ها: OD: φ6-1800mm ، ضخامت دیواره از 1-35 میلی متر است.

شرط تمام شده کالاها: جعل گرم / نورد گرم + آنیل / عادی سازی + معتدل / خاموش + معتدل / هر شرایطی براساس نیاز مشتری

شرایط سطح: مقیاس پذیر (پایان کار داغ) / زمین / ماشینکاری خشن / ماشینکاری ریز / بر اساس نیاز مشتری

کوره های پردازش متالورژی: قوس الکترود + LF / VD / VOD / ESR / الکترود قابل استفاده با خلا.

بازرسی اولتراسونیک: بازرسی اولتراسونیک 100٪ برای هرگونه نقص و یا بر اساس نیاز مشتری خدمات عالی برای انواع صنایع ، با مزایای فناوری ، تجهیزات و قیمت.

ما به شما با صداقت احترام و حرفه ای بودنمان خدمات میدهیم.

Standards – Alloy 303

ASTM/ASME:UNS S30300

EURONORM:FeMi35Cr20Cu4Mo2

DIN:1.4305

خواص عمومی

Alloy 303 is a non-magnetic, austenitic stainless steel that is not hardenable by heat treatment. It is the free machining modification of the basic 18% chromium / 8% nickel stainless steel. Alloy 303 was specially designed to exhibit improved machinability while maintaining good mechanical and corrosion resistant properties Due to the presence of sulfur in the steel composition, Alloy 303 is the most readily machineable austenitic stainless steel; however, the sulfur addition does lower Alloy 303’s corrosion resistance to below that of Alloy 304. Like other austenitic grades, Alloy 303 demonstrates excellent toughness, although the sulfur does reduce this a little as well.

برنامه های کاربردی

Alloy 303 is frequently used in applications that require parts to be heavily machined. Some examples include:

1、Nuts and bolts

2、Aircraft fittings

3、Gears

4、Screws

5、Shafts

6、Electrical switchgear components

7、Bushings

مقاومت در برابر خوردگی

• Good resistance to mildly corrosive atmospheres, but significantly less than Alloy 304
• When additional sulfur is added to improve machinability, it can often slightly reduce corrosion resistance
• In most dry and mild corrosive environments, Alloy 303 is comparable to other unmodified alloys
• Should not be exposed to moist, marine environments as it is subject to rapid-pitting corrosion and a rust film will tend to form
• Like other common austenitic stainless steels, it is subject to corrosion cracking in chloride environments above 60^oC

مقاومت در برابر حرارت

• Good oxidation resistance at temperatures up to 1700^oF (927 ^oC)
• Continuous use at temperatures above 1400^oF (760^oC) is not usually recommended due to carbide precipitation which can lead to irregular scaling
• Does not have a low carbon content so it is also vulnerable to sensitisation

Chemical Properties:

%	Cr	Ni	C	Si	Mn	P	S	Mo	Fe
303	min: 17.0 max:19.0	min: 8.0 max: 10.0	0.15 حداکثر	1.00 حداکثر	2.0 حداکثر	0.20 حداکثر	0.15 دقیقه	0.75	تعادل

ویژگی های مکانیکی:

درجه	استحکام کششی ksi (min.)	Yield Strength 0.2% Offset ksi (min.)	Elongation - % in 50 mm (min.)	سختی (Brinell) MAX	سختی (Rockwell B) MAX
303	75	30	35	228