AISI 8620 / 1.7321 / DIN 20MoCr4 ،
- درجه:
کلیک کنید برای ارسال ایمیل
به اشتراک گذاری این آگهی
مشخصات، شیمیایی و عملکرد مکانیکی
تعیین بر اساس استاندارد
| نام تجاری | راون شماره | حصیر نه | DIN | EN | AISI |
| 20MOCR4 | 763 | 1.7321 | 20MoCr4 | 20MoCr4KD | 8620 |
ترکیب شیمیایی (در وزن٪)
| C | Si | Mn | Cr | Mo | Ni | V | W | دیگران |
| 0.20 | حداکثر 0.40 | 0.85 | 0.45 | 0.45 | - | - | - | - |
شرح
One of the most popular and widely used carborizing steels available. 20MoCr4 is a hardenable chromium, molybdenum, nickel low alloy steel often used for carburizing to develop a case-hardened part. This case-hardening will result in good wear characteristics.
برنامه های کاربردی
Gears, shafts and other applications where a hard carborized case and a tough core are desired.
خصوصیات بدنی (مقادیر آواریژ) در دمای محیط
مدول الاستیسیته [103 x N / mm2]: 210
تراکم [g / cm3]: 7.85
ضریب گسترش حرارتی خطی 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC |
| 11.1 | 12.1 | 12.7 | 12.9 | 13.5 |
آنیل نرم
گرما تا 650-700oC ، آرام آرام. این کار حداکثر سختی برینل 207 را ایجاد می کند.
حرارت درمانی
| رفتار | درجه حرارت | خنک سازی |
| Case hardening | 880-980oC | Oil (water), hot bath 160-250oC |
| Carburising | 880-980oC | Oil (water), hot bath 160-250oC |
| Direct hardening | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 780-820oC | Oil, hot bath 160-250oC |
| خستگی | 150-200oC | هوا |
آهنگری
دمای تشکیل گرم: 1050-850oC.
ماشین کاری
Machining is done prior to carburizing to within as close a tolerance as possible. Finish machining, after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment – after carburizing machining is usually limited to grinding.
جوش
The alloy may be welded by conventional methods, usually gas or arc welding. Preheating at 200oC is beneficial and subsequent heating after welding is recommended – consult the approved weld procedure for the method used.
کار سرد
The alloy may be cold worked in the annealed condition by conventional methods. Cold working, as with machining, should be done to as close a tolerance as possible before heat treatment or carburizing.
فرم های تولید شده: لطفاً برنامه فروش بعدی را ببینید.
سلب مسئولیت
اطلاعات و داده های ارائه شده در اینجا مقادیر معمولی یا متوسط هستند و ضامن حداکثر یا حداقل مقادیر نیستند. برنامه هایی که به طور خاص برای مطالب توصیف شده در اینجا پیشنهاد شده اند ، صرفاً به منظور تصویر سازی ساخته شده اند تا خواننده بتواند ارزیابی خودش را انجام دهد و به عنوان ضمانت ، بیان یا ضمنی از تناسب اندام برای این یا بچه های دیگر در نظر گرفته نشده است. هیچ اظهار نظری وجود ندارد که گیرنده این ادبیات به عنوان در دسترس بودن ، نسخه های به روز شده را دریافت کند.