فولاد AISI M1 / 1.3346 / DIN S2-9-1
- درجه:
کلیک کنید برای ارسال ایمیل
به اشتراک گذاری این آگهی
مشخصات، شیمیایی و عملکرد مکانیکی
تعیین بر اساس استاندارد
| نام تجاری | راون شماره | حصیر نه | DIN | EN | AISI |
| BRM1 | 877 | 1.3346 | S2-9-1 | - | M1 |
ترکیب شیمیایی (در وزن٪)
| C | Si | Mn | Cr | Mo | Ni | V | W | دیگران |
| 0.82 | حداکثر 0.45 | حداکثر 0.40 | 3.85 | 8.60 | - | 1.15 | 1.75 | - |
شرح
M1 is a molybdenum, chromium, vanadium alloy tool steel generally known as a Molybdenum High Speed Tool Steel. It is on of the most widely available tool steels in use today. It is similar in properties to the tungsten tool steels (T series) at a lower. Very tough high-speed Mo steel good grindability.
برنامه های کاربردی
Twist drills, thread cutting tools, hobs and dies for broaching and cold flow pressing, cross recess dies for screw manufacture, cold rolling for e.g. Sendzimir equipment.
خصوصیات بدنی (مقادیر آواریژ) در دمای محیط
مدول الاستیسیته [103 x N / mm2]: 217
تراکم [g / cm3]: 8.0
هدایت حرارتی [W / mK]: 19.0
مقاومت الکتریکی [اهم میلی متر2/ m]: 0.60
ظرفیت حرارتی خاص [J / gK]: 0.46
ضریب گسترش حرارتی خطی 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC | 20-700oC |
| 11.0 | 11.5 | 11.9 | 12.3 | 12.4 | 12.5 | 12.5 |
نمودار تحول خنک کننده مداوم (CCT)
برای بزرگنمایی نمودار ، روی تصویر کلیک کنید.
آنیل نرم
گرما تا 820-850oC, cool slowly in furnace to 550oC then air. This will produce a maximum Brinell hardness of 262.
تسکین استرس
Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
استحکام سیستم عامل ها
0 Harden from a temperature of 1180-1219oC followed by air or oil quenching or warm bath at 550oج - سختی پس از خاموش شدن 64-66 HRC است.
خستگی
Tempering temperature: 530 – 560oC, at least 2x for at least 63 HRC.
نمودار دما
برای بزرگنمایی نمودار ، روی تصویر کلیک کنید.
آهنگری
دمای تشکیل گرم: 1100-900oC.
Cold Working
This alloy may be cold worked in the annealed condition.
ماشین کاری
M1 is classified as a “medium” machinable alloy. Machining should be accomplished prior to hardening heat treatment followed by finish grinding. It has a rating of 50% that of the water hardening (W group) low alloy tool steels in regard to machinability.
مقاومت در برابر خوردگی
This is not a corrosion resistant alloy. In use as tooling it is often coated with oil to prevent rusting. A light film of oil. or protective wrapping, is essential to keep it free from corrosion.
جوش
Consult the alloy supplier for information on weld procedures.
فرم های تولید شده: لطفاً برنامه فروش بعدی را ببینید.