فولاد ابزار T6 با سرعت بالا ASTM (UNS T12006)
- درجه:
کلیک کنید برای ارسال ایمیل
به اشتراک گذاری این آگهی
مشخصات، شیمیایی و عملکرد مکانیکی
ASTM T6 High Speed tool steel also belongs to tungsten type high speed steels in ASTM A600 specification. ASTM T6 Tool Steel is similar to T5 Tool Steel, but T-6 steel has more Cobalt and Tungsten content than T5 tool steels, and T6 tool steel is better in high temperature hardness and wear resistance.
We are one of best supplier of AISI T6 tool steel. We supply exactly what you need about ASTM T6 HSS tool steel.
1.AISI T6 Tool Steel Supply Range
T6 نوار گرد فولادی: قطر 2mm - 800mm
T6 فولاد تخت: ضخامت 2-400mm x عرض 10-600mm
ورق فولادی ابزار T6: ضخامت 2-600mm x عرض 200-610mm
سطح نهایی: مشکی ، ماشین آلات خشن ، چرخانده یا مطابق با شرایط مورد نیاز.
2.Standard of AISI T6 Tool Steel High Speed
| کشور | ایالات متحده |
| استاندارد | ASTM A600 |
| درجات | T6 / T12006 |
3.ASTM High Speed T6 Steel Chemical Composition Properties
| ASTM A600 | C | Mn | P | S | Si | Cr | V | Mo | W | Co | ||||||||
| T6 / T12006 | 0.75 | 0.85 | 0.20 | 0.40 | 0.03 | 0.03 | 0.20 | 0.40 | 4.00 | 4.75 | 1.50 | 2.10 | 0.40 | 1.00 | 18.50 | 21.00 | 11.00 | 13.00 |
4.AISI T6 Tool Steels Mechanical Properties
خصوصیات فیزیکی فولاد ابزار T6
- تراکم (lb / cu. داخل) 0.322
- جاذبه خاص 8.89
- نقطه ذوب (Deg F) 2620
- مدول تنش کشش 29
Mechanical Properties of T-6 Tool Steel
|
قدرت اثبات Rp0.2 |
استحکام کششی Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture الف (٪) |
کاهش سطح مقطع شکستگی Z (٪) |
شرایط تحت درمان با گرما | Brinell hardness (HBW) |
| 633 (≥) | 366 (≥) | 43 | 23 | 41 | راه حل و پیری ، پخت و پز ، پخش مداوم ، Q + T و غیره | 134 |
5.Forging از فولاد با سرعت بالا ASTM T6
Forge at 1162℃ down to 1010℃. Do not forge below 982℃.
عملیات حرارتی فولادی با سرعت بالا 6.ASTM T6
Preheat TT steels to 815℃ and then heat rapidly to 1273 – 1287℃ and hold at temperature for 2 to 5 minutes. Quench in air, salt bath, or oil.
Annealing of Steel T-6
Anneal at 885℃ and slow cool in the furnace at a rate less than 4℃ per hour.
Tempering of T6 Steel
Temper T6 at 537℃ to 593℃ for Rockwell C of 65 to 60.
7.Applications of AISI T6 High Speed Steel
AISI T6 high speed steels are mainly used for cutting applications such as drills, milling processes, cutting tools, reamers, etc.
Some typical applications of T6 tool steel are as below:
- ابزارهای چرخش و شکاف
- ابزار بروشینگ
- Reamers
- موضوع می میرد
- دریل پیچ و تاب
- نوار
- Broaches etc
Together with ASTM T6 tool steel, we could also supply you T-1 steels, T2 steel, T4 tool steel, T5 steels, T15 steel, M2 & M42steel etc. You are welcome to send your requests to us anytime. We are a better choice for you.