Especificación, química y rendimiento mecánico
Podemos producir 1.0402, DIN C22, Varillas redondas de acero inoxidable AISI 1020, 1.0402, DIN C22, AISI 1020 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong production experience, strict control 1.0402, DIN C22, AISI 1020 chemical composition and 1.0402, DIN C22, AISI 1020 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.
especificación de la producción
Barra redonda de acero: 1mm a 3500mm
Acero de forma cuadrada: 1mm a 4000mm
Placa de acero:0.1mm a 4000mm
AN 10mm a 2500mm
Lenth: Podemos suministrar cualquier préstamo basado en los requisitos del cliente.
Forja: ejes con flancos / tuberías / tubos / babosas / rosquillas / cubos / otras formas
Tubos: OD: φ6-1800mm, con espesores de pared que van desde 1-35 mm.
Condición de los productos terminados: forjado en caliente / laminado en caliente + recocido / normalización + templado / temple + templado / cualquier condición basada en los requisitos del cliente
Condiciones de la superficie: escalado (acabado de trabajo en caliente) / rectificado / mecanizado en bruto / mecanizado fino / según los requisitos del cliente
Hornos para procesamiento metalúrgico: arco de electrodos + LF / VD / VOD / ESR / Vacío electrodo consumible.
Inspección ultrasónica: 100% inspección ultrasónica para cualquier imperfección o basada en los requisitos del cliente Excelente servicio para todo tipo de industrias, con ventajas de tecnologías, equipos y precios.
Le servimos con nuestra honestidad, integridad y profesionalidad.
Designación por normas
| XNUMX- Cuales serian las circunstancias por las cuales tu producto cambiaria de precio? (Obligatorio - Publico) | LH No. | Estera. No. | DIN | EN | AISI |
| C22 | 514 | 1.0402 | C22 | - | 1020 |
Composición química (en% en peso)
| C | Si | Mn | Cr | Mo | Ni | V | W | Otros |
| 0.22 | máx. 0.40 | 0.55 | máx. 0.40 | máx. 0.10 | máx. 0.40 | - | - | (Cr + Mo + Ni) = máx. 0.63 |
Descripción
C22 is one of the very commonly used plain carbon steels. It has a nominal carbon content of 0.22% with approximately 0.55% manganese. It is a good combination of strength and ductility and may be hardened or carburized.
Aplicaciones
C22 steel is used for simple structural application such as cold headed bolts. It is often used in the case hardened condition.
Propiedades físicas (valores promedio) a temperatura ambiente
Módulo de elasticidad [103 x N / mm2]: 210
Densidad [g / cm3]: 7.70
Conductividad térmica [W / mK]: 51.9
Resistencia eléctrica [Ohm mm2/ m]: 0.11
Capacidad calorífica específica [J / gK]: 0.46
Recocido suave
Calentar a 870-980oC, cool slowly. This will produce a minimum tensile strength of 450 Mpa.
Alivio del estrés
El alivio de la tensión para eliminar las tensiones de mecanizado se debe realizar calentando a aprox. 540oC, manteniendo durante 1-2 horas al calor, seguido de enfriamiento por aire. Esta operación se realiza para reducir la distorsión durante el tratamiento térmico.
Endurecimiento
Endurecerse a partir de una temperatura de 820-870oC seguido de enfriamiento con agua.
Temperamento
Tempering temperature: Please ask.
Forjando
Temperatura de formación en caliente: 1200-950oC.
maquinabilidad
Machinability is good at 65% compared to 1112 carbon steel as 100% baseline.
Resistencia a la Corrosión
Not corrosion resistant. The steel will rust unless protected.
Soldadura
Readily weldable by all of the standard methods.
Trabajo en frío
C22 steel is readily cold worked by all conventional methods. A stress relief anneal may be needed after extensive cold work.
Las propiedades mecánicas