AISI M7 / 1.3348 / DIN S2-9-2
- Grado:
Está interesado en este anuncio? En contacto con el vendedor!
Janet Chang + 86-185 1669 6028
Click To Contactar al Anunciante
Comparte este anuncio
Especificación, química y rendimiento mecánico
Designación por normas
| XNUMX- Cuales serian las circunstancias por las cuales tu producto cambiaria de precio? (Obligatorio - Publico) | Ravne No. | Estera. No. | DIN | EN | AISI |
| BR885 | 885 | 1.3348 | S2-9, 2 | HS2-9-2 | M7 |
Composición química (en% en peso)
| C | Si | Mn | Cr | Mo | Ni | V | W | Otros |
| 0.98 | máx. 0.70 | máx. 0.40 | 4.00 | 8.70 | - | 1.95 | 1.80 | - |
Descripción
M7 is one of the High Speed Tool Steels in the molybdenum alloy family, with tungsten, chromium and vanadium for strengthening. It has good hardenability and is very wear resistant. Very high resistance to softening at elevated temperatures and good toughness. Deep hardening response.
Aplicaciones
M7 is widely used for cutting tools in machining operations. Sendzimir rolls, segment and circular cutters, profile cutting tools, thread cutting drills and cold forming tools.
Propiedades físicas (valores promedio) a temperatura ambiente
Módulo de elasticidad [103 x N / mm2]: 217
Densidad [g / cm3]: 8.30
Conductividad térmica [W / mK]: 19.0
Resistencia eléctrica [Ohm mm2/ m]: 0.65
Capacidad calorífica específica [J / gK]: 0.46
Coeficiente de expansión térmica lineal 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC | 20-700oC |
| 11.7 | 12.5 | 12.9 | 13.2 | 13.4 | 13.4 | 13.4 |
Continuous Cooling Transformation (CCT) Diagram
Click the image to enlarge the diagram.
Time-Temperature Transformation (TTT) Diagram
Click the image to enlarge the diagram.
Recocido suave
Calentar a 820-880oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230-280.
Endurecimiento
Heat up to 450-600oC, preheat to 850oC and then to 1050oC. Harden from a temperature of 1180-1220oC followed by oil, air quenching or warm bath at 550oC. Hardness after quenching is 64-66 HRC.
Temperamento
Tempering temperature: 3 x 1 hour at 540-560oC. Hardness after tempering is min 64 HRC.
Forjando
Temperatura de formación en caliente: 1100-900oC.
Cold Working: In the annealed condition M7 may be cold worked by conventional methods.
maquinabilidad
Machinability is medium, rating about 60% that of the W group water hardening low alloy tool steels at 100% for comparison.
Resistencia a la Corrosión
Although this alloy contains chromium and molybdenum it is still a steel and thus will corrode. It should be protected from rusting.
Soldadura
This is a complex alloy but is weldable. Consult the supplier for procedures and details.
Formularios fabricados: consulte el Programa de ventas dimensionales.
Términos y Condiciones
La información y los datos presentados aquí son valores típicos o promedio y no son garantía de valores máximos o mínimos. Las aplicaciones específicamente sugeridas para el material descrito en este documento se realizan únicamente con el propósito de ilustrar para permitir al lector hacer su propia evaluación y no tienen la intención de ser garantías, expresas o implícitas, de idoneidad para estas u otras pupilas. No hay representación de que el destinatario de esta literatura reciba ediciones actualizadas a medida que estén disponibles.