AISI M7 / 1.3348 / DIN S2-9-2
- Grade:
Cliquez pour envoyer un courriel Vendeur
Partager cette annonce
Spécification, Chemical & Performance mécanique
Désignation par normes
| Marque | Ravne No. | Tapis. Non. | DIN | EN | AISI |
| BR885 | 885 | 1.3348 | S2-9-2 | HS2-9-2 | M7 |
Composition chimique (en% en poids)
| C | Si | Mn | Cr | Mo | Ni | V | W | Autres |
| 0.98 | max. 0.70 | max. 0.40 | 4.00 | 8.70 | - | 1.95 | 1.80 | - |
Description
M7 is one of the High Speed Tool Steels in the molybdenum alloy family, with tungsten, chromium and vanadium for strengthening. It has good hardenability and is very wear resistant. Very high resistance to softening at elevated temperatures and good toughness. Deep hardening response.
Applications
M7 is widely used for cutting tools in machining operations. Sendzimir rolls, segment and circular cutters, profile cutting tools, thread cutting drills and cold forming tools.
Propriétés physiques (valeurs moyennes) à température ambiante
Module d'élasticité [103 x N / mm2]: 217
Densité [g / cm3]: 8.30
Conductivité thermique [W / mK]: 19.0
Résistivité électrique [Ohm mm2/ m]: 0.65
Capacité thermique spécifique [J / gK]: 0.46
Coefficient de dilatation thermique linéaire 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC | 20-700oC |
| 11.7 | 12.5 | 12.9 | 13.2 | 13.4 | 13.4 | 13.4 |
Diagramme de transformation en refroidissement continu (CCT)
Cliquez sur l'image pour agrandir le diagramme.
Diagramme de transformation temps-température (TTT)
Cliquez sur l'image pour agrandir le diagramme.
Recuit doux
Chauffer à 820-880oC, cool slowly in furnace. This will produce a maximum Brinell hardness of 230-280.
durcissement
Heat up to 450-600oC, preheat to 850oC and then to 1050oC. Durcir à une température de 1180-1220oC followed by oil, air quenching or warm bath at 550oC. La dureté après trempe est 64-66 HRC.
Tempérer
Tempering temperature: 3 x 1 hour at 540-560oC. Hardness after tempering is min 64 HRC.
Forger
Température de formage à chaud: 1100-900oC.
Cold Working: In the annealed condition M7 may be cold worked by conventional methods.
Usinabilité
Machinability is medium, rating about 60% that of the W group water hardening low alloy tool steels at 100% for comparison.
Résistance à la corrosion
Although this alloy contains chromium and molybdenum it is still a steel and thus will corrode. It should be protected from rusting.
Soudage
This is a complex alloy but is weldable. Consult the supplier for procedures and details.
Formulaires fabriqués: veuillez consulter le programme de vente dimensionnel.
Disclaimer
Les informations et données présentées ici sont des valeurs typiques ou moyennes et ne sont pas une garantie de valeurs maximales ou minimales. Les applications spécifiquement suggérées pour le matériel décrit ici sont faites uniquement à des fins d'illustration pour permettre au lecteur de faire sa propre évaluation et ne sont pas conçues comme des garanties, expresses ou implicites, d'adéquation à ces fins ou à d'autres fins. Rien ne garantit que le destinataire de cette documentation recevra des éditions mises à jour à mesure qu'elles deviendront disponibles.