UNS S31254, 1.4547, SUS 312L - Super Austenitic Stainless Steel
SUS 312L, UNS S31254 is a high corrosion resistant austenitic stainless steel with a high nickel, high chromium, high molybdenum alloy design, and provides excellent corrosion resistance in severe corrosion environments such as high temperature seawater. Depending on the environment, this stainless steel offers high economy combined with corrosion resistance comparable to that of Nickel alloy and pure titanium. Shanghai BoZhong Steel Group supplies this product in plate, sheet, strip form, Pipe and Flange.
If you have artwork or drawing, we could produce basing on your request.
Manque de maniabilité
L'usinabilité à chaud et à froid du SUS 312L est fondamentalement la même que celle des aciers inoxydables austénitiques standard tels que le type 304, le type 316, etc.
Soudabilité
Diverses méthodes de soudage sont applicables de la même manière qu'avec les aciers inoxydables austénitiques standard, y compris le soudage à l'arc avec blindage métallique, le soudage TIG et le soudage plasma. Un consommable de soudage en alliage 276 doit être utilisé.
Usinabilité
Comme caractéristique des aciers inoxydables à haute teneur en Ni, bien que l'usinage soit difficile par rapport aux aciers inoxydables austénitiques standard, il est plus facile qu'avec les alliages à base de Ni. Dans la mesure du possible, un outil ultra-dur doit être utilisé dans l'usinage. Il est également conseillé d'utiliser une vitesse d'avance plus lente et une profondeur de coupe plus profonde.
Traitement thermique
Because sus 312L is an austenitic stainless steel, heat treatment is equivalent to that with the standard austenitic stainless steels. The following heat treatment conditions are normally used:
- Traitement thermique de la solution: 1125 ~ 1175 ℃; Eau froide
Le marinage
A mixture of nitric acid and hydrofluoric acid is used in pickling. However, due to the high corrosion resistance of SUS 312 L, scale is somewhat difficult to remove in comparison with Type 304. Therefore, the material should be immersed in an alkaline solution before pickling, or if possible, shot blasting is extremely effective.
Applications
- Environnements d'eau de mer: Structures marines, systèmes de dessalement d'eau de mer, échangeurs de chaleur utilisant de l'eau de mer, tubes de condenseur, etc.
- Usines de pâtes et papiers: divers types de systèmes de blanchiment, d'épurateurs, etc.
- Usines de produits médicaux et pharmaceutiques: séparateurs centrifuges, réservoirs de réaction, etc.
Certificat
Il est possible de fabriquer UNS S31254 conformément à la norme NORSOK ci-dessous. L'épaisseur est jusqu'à 40mm.
- M-650
- M-630 MDS R15