AISI 4337 / 4340 / 1.6582 / 34CrNiMo6

मानकों द्वारा पदनाम

रासायनिक संरचना (वजन में%)

विवरण
VCNMO150 is a heat treatable, low alloy steel containing nickel, chromium and molybdenum. It is known for its toughness and capability of developing high strength in the heat treated condition while retaining good fatigue strength. A very popular, versatile steel. It can be heat-treated to produce a wide range of tensile strength in moderate sections.

अनुप्रयोगों
Typical applications are for structural use, such as aircraft landing gear, power transmission gears and shafts and other structural parts, general engineering parts, hrough-hardened gears, connecting rods and bolts, gun barrels.

परिवेश के तापमान पर भौतिक गुण (एवरेज मान)
लोच का मापांक [10³ x एन / मिमी²]: 210
घनत्व [जी / सेमी³]: 7.84
थर्मल चालकता [W / mK]: 37.7
विशिष्ट ताप क्षमता [J / gK]: 0.46

Environmental resistance
Flammability: very good
Fresh water: good
Organic solvent: very good
Oxidation at 500^oC: good
Sea water: average
Strong acid: poor
Strong alkalis: poor
Wear: very good
Weak acid: average
Weak alkalis: good
Minimum service temperature: -73.2 to -42.2^oC
Maximum service temperature: 613-653^oC

सामान्य
सामान्य तापमान: 850-880^oC.

तनाव राहत
मशीनिंग के तनाव को दूर करने के लिए तनाव से राहत को लगभग गर्म करके किया जाना चाहिए। 650^oC, ताप पर 1-2 घंटे के लिए होल्डिंग, इसके बाद हवा को ठंडा किया जाता है। यह ऑपरेशन गर्मी उपचार के दौरान विकृति को कम करने के लिए किया जाता है।

सख्त
830-860 के तापमान से कठोर^oC followed by oil quenching. Qenching temperature in the end-quench test is 850^oC.

टेम्परिंग
तापमान का तापमान: 540-660^oC.

बुझती और टेम्पर्ड स्थिति में यांत्रिक गुण

मिमी से बुझी हुई दूरी से

फोर्जिंग
गर्म बनाने का तापमान: 1100-900^oC.

मशीन की
Machining is best done with this alloy in the annealed or normalized and tempered condition. It can be machined by all conventional methods.

संक्षारण प्रतिरोध
This is a low alloy steel and not a corrosion resistant alloy. Protective coating should be used.

वेल्डिंग
The alloy can be fusion or resistance welded. Preheat and post heat weld procedures should be followed when welding this alloy by established methods.

ठंड काम कर रही है
The VCNMO150 alloy may be cold worked, in the annealed condition, by conventional methods and tooling. It has good ductility.

निर्मित प्रपत्र: कृपया आयामी बिक्री कार्यक्रम देखें।

अस्वीकरण
यहां प्रस्तुत जानकारी और डेटा विशिष्ट या औसत मूल्य हैं और अधिकतम या न्यूनतम मूल्यों की गारंटी नहीं है। यहां वर्णित सामग्री के लिए विशेष रूप से सुझाए गए एप्लिकेशन केवल चित्रण के उद्देश्य से पाठक को अपना मूल्यांकन करने में सक्षम बनाने के लिए बनाए जाते हैं और इन या अन्य विद्यार्थियों के लिए फिटनेस के वारंटियों के रूप में व्यक्त या निहित नहीं हैं। इस बात का कोई प्रतिनिधित्व नहीं है कि इस साहित्य को प्राप्त करने वाले उपलब्ध होने के रूप में अद्यतन संस्करण प्राप्त करेंगे।