Composizione chimica
|
%
|
Ni
|
Cr
|
Mo
|
Fe
|
Co
|
W
|
C
|
Mn
|
Si
|
P
|
S
|
Al
|
Cu
|
La
|
B
|
|
verbale
|
equilibrio
|
14.5
|
14.0
|
|
|
|
|
0.30
|
0.20
|
|
|
0.10
|
|
0.01
|
|
|
max
|
17.0
|
16.5
|
3.0
|
2.0
|
1.00
|
0.020
|
1.00
|
0.75
|
0.020
|
0.015
|
0.50
|
0.35
|
0.10
|
0.015
|
Proprietà fisiche
| Densità |
7.75 g / cm3 |
| Intervallo di fusione |
1404-1440 ℃ |
Caratteristiche: 17-4PH is a chromium-nickel-copper precipitation hardening martensitic stainless steel that combines oxidation and corrosion resistance comparable to 304 in most environments with high strength and hardness. It is the most widely used of all the precipitation hardening stainless steels, and is more cost effective than many high nickel non-ferrous alloys in some
Applicazioni. 17-4PH cannot be used at temperatures above 300℃ and at cryogenic temperatures. It is magnetic.
Industria aerospaziale, utensili manuali biomedici, attrezzature per la lavorazione chimica e alimentare, trattamento e stoccaggio di scorie nucleari, lavorazione generale dei metalli e attrezzature per cartiere.