Specifiche, Chemical & prestazioni meccaniche
Designazione secondo gli standard
| Brand | Ravne No. | Stuoia. No. | DIN | EN | AISI |
| 20MOCR4 | 763 | 1.7321 | 20MoCr4 | 20MoCr4KD | 8620 |
Composizione chimica (in% in peso)
| C | Si | Mn | Cr | Mo | Ni | V | W | Altri |
| 0.20 | max. 0.40 | 0.85 | 0.45 | 0.45 | - | - | - | - |
Descrizione
One of the most popular and widely used carborizing steels available. 20MoCr4 is a hardenable chromium, molybdenum, nickel low alloy steel often used for carburizing to develop a case-hardened part. This case-hardening will result in good wear characteristics.
Applicazioni
Ingranaggi, alberi e altre applicazioni in cui sono desiderati una custodia rigida e un nucleo resistente.
Proprietà fisiche (valori medi) a temperatura ambiente
Modulo di elasticità [103 x N / mm2]: 210
Densità [g / cm3]: 7.85
Coefficiente di dilatazione termica lineare 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC |
| 11.1 | 12.1 | 12.7 | 12.9 | 13.5 |
Ricottura Morbida
Riscalda a 650-700oC, raffreddati lentamente. Ciò produrrà una durezza Brinell massima di 207.
Trattamento termico
| Trattamento | Temperatura | Raffreddamento |
| Case hardening | 880-980oC | Oil (water), hot bath 160-250oC |
| Carburising | 880-980oC | Oil (water), hot bath 160-250oC |
| Direct hardening | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 780-820oC | Oil, hot bath 160-250oC |
| tempra | 150-200oC | Aria |
Forgiatura
Temperatura di formatura a caldo: 1050-850oC.
lavorabilità
Machining is done prior to carburizing to within as close a tolerance as possible. Finish machining, after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment – after carburizing machining is usually limited to grinding.
Saldatura
The alloy may be welded by conventional methods, usually gas or arc welding. Preheating at 200oC is beneficial and subsequent heating after welding is recommended – consult the approved weld procedure for the method used.
Lavorazione a freddo
The alloy may be cold worked in the annealed condition by conventional methods. Cold working, as with machining, should be done to as close a tolerance as possible before heat treatment or carburizing.
Moduli prodotti: consultare il programma di vendita dimensionale.
Termini e condizioni
Le informazioni e i dati qui presentati sono valori tipici o medi e non sono garanzia di valori massimi o minimi. Le applicazioni specificamente suggerite per il materiale qui descritto sono fatte esclusivamente a scopo illustrativo per consentire al lettore di effettuare la propria valutazione e non sono intese come garanzie, espresse o implicite, di idoneità per questi o altri alunni. Non vi è alcuna dichiarazione che il destinatario di questa letteratura riceverà edizioni aggiornate non appena saranno disponibili.