AISI 1010, 1.0301, DIN Ck10,
- 학년 :
사양, 화학 및 기계 성능
우리는 생산할 수 있습니다 1.1121, DIN Ck10, AISI 1010 stainless steel round rods, 1.1121, DIN Ck10, AISI 1010 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong production experience, strict control 1.1121, DIN Ck10, AISI 1010 chemical composition and 1.1121, DIN Ck10, AISI 1010 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.
생산 사양
라운드 바 스틸 : 1mm ~ 3500mm
정사각형 강철 : 1mm ~ 4000mm
강판 : 0.1mm ~ 4000mm
너비 : 10mm ~ 2500mm
Lenth : 고객 요구 사항에 따라 모든 lenth를 공급할 수 있습니다.
단조 : 측면 / 파이프 / 튜브 / 슬러그 / 도넛 / 큐브 / 기타 형태의 샤프트
튜브 : OD : φ6-1800mm, 벽 두께는 1-35mm 범위입니다.
완제품 상태 : 열간 단조 / 열간 압연 + 어닐링 / 정규화 + 템퍼링 / 소입
표면 조건 : 스케일링 (열간 가공) / 연삭 / 황삭 / 정밀 가공 / 고객 요구 사항에 따라
야금 공정 용광로 : 전극 아크 + LF / VD / VOD / ESR / 진공 소모품 전극.
초음파 검사 : 불완전하거나 고객의 요구에 따라 100 % 초음파 검사 기술, 장비 및 가격의 장점을 가진 모든 종류의 산업에 대한 우수한 서비스.
우리는 정직, 성실 및 전문성을 제공합니다.
표준에 의한 지정
| 상표명 | LH 번호 | 매트. 아니. | DIN | EN | AISI |
| CK10 | 605 | 1.0301 | C10 | C10 | 1010 |
화학 성분 (중량 %)
| C | Si | Mn | Cr | Mo | Ni | V | W | 기타 |
| 0.10 | 최대. 0.40 | 0.45 | - | - | - | - | - | - |
설명
CK10 is a plain carbon steel with a nominal 0.10% carbon content. It is a relatively low strength steel but it may be quenched and tempered for increased strength.
도금 두께 측정기
The low carbon steels, such as CK10, are used for applications such as cold headed fasteners and bolts.
주변 온도에서의 물리적 특성 (평균값)
탄성 계수 [103 x N / mm2] : 210
밀도 [g / cm3] : 7.85
소프트 어닐링
800-840로 가열oC, 천천히 식히십시오.
경화
This steel is generally used in the annealed or case hardened condition. It may be heat treated, quenched and tempered but the cost for so doing is generally not worth the result.
템퍼링
템퍼링 온도 : 320-530oC.
단조
열간 성형 온도 : 1050-850oC.
가공성
Machinability of CK10 steel is fairly good, especially in the cold drawn or cold worked condition. Based upon carbon steel AISI 1112 as a reference that is considered 100% machinable (easily machined) the CK10 steel has a rating of 55%.
부식 저항
This is a plain carbon steel and has no corrosion resistance. It will rust unless protected.
용접
CK10 steel may be welded by all of the standard welding techniques.
냉간 가공
CK10 is easily cold worked by traditional means. Following severe cold working a stress relief, or full, anneal should be performed.
기계적 성질
열처리