AISI A182 Grade F11/Mat.No. 1.7335/ DIN 13CrMo44,

We can produce 1.7335, DIN 13CrMo44, AISI A182 Grade F11 stainless steel round rods, 1.7335, DIN 13CrMo44, AISI A182 Grade F11 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong production experience, strict control 1.7335, DIN 13CrMo44, AISI A182 Grade F11 chemical composition and 1.7335, DIN 13CrMo44, AISI A182 Grade F11 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.

생산 사양

Round bar steel: 1mm에 3500mm

Square-shape steel: 1mm에 4000mm

Plate steel:0.1mm에 4000mm

폭 : 10mm에 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

단조 : Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-1800mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

우리는 정직, 성실 및 전문성을 제공합니다.

표준에 의한 지정

상표명	라브 네	매트. 아니.	DIN	EN	AISI
13CRMO44	762	1.7335	13CrMo44	13CrMo4-5	A 182 Grade F11

화학 성분 (중량 %)

C	Si	Mn	Cr	Mo	Ni	V	W	기타
0.14	최대. 0.40	0.55	0.98	0.60	-	-	-	max. Cu = 0.30

설명
합금 특수 구조용 강. > 0.35 % Mo 이상의 Cr-Mo- 스틸.

도금 두께 측정기
High-temperature structural steel: Collectors, water boiler and superheater tubes (530^o기음).

주변 온도에서의 물리적 특성 (평균값)
탄성 계수 [10³ x N / mm²] : 210
밀도 [g / cm³] : 7.85

소프트 어닐링
680-720로 가열^oC, cool slowly in furnace.

경화
910-940의 온도에서 강화^oC followed by oil or air quenching.

템퍼링
템퍼링 온도 : 650-720^oC.

Mechanical Properties in Hardened and Tempered Condition

Diameter in mm	0.2 % 내력 (N / mm2)	인장 강도 (N / mm2)	신장률 (%)	Impact strength (J)
60까지	295	440-590	20	44
61-90	285	440-590	20	44
91-150	275	440-590	20	44

0.2 % Proof Stress (N/mm²) vs. Temperature

100oC	150oC	200oC	250oC	300oC	350oC	400oC	450oC	500oC
260	245	240	230	215	200	190	180	175
250	240	230	220	205	190	180	170	165
250	235	220	210	195	180	170	160	155

1 % Creep Limit (N/mm²) vs. Temperature (^oC)

시간	450oC	460oC	480oC	500oC	520oC	540oC	560oC
10 000	245	228	193	157	122	90	64
100 000	191	172	133	98	70	46	30

Creep Rapture Strength (N/mm²) vs. Temperature (^oC)

시간	450oC	460oC	480oC	500oC	520oC	540oC	560oC
10 000	370	348	304	239	179	129	91
100 000	285	251	190	137	94	61	40
200 000	260	226	167	115	76	50	32

단조
열간 성형 온도 : 1100-850^oC.