AISI 8620 / 1.7321 / DIN 20MoCr4,
- Grade:
Clique Para Email do Vendedor
Partilhar este anúncio
Especificação, Chemical & desempenho mecânico
Designação por normas
| Marca | Ravne No. | Esteira. Não. | DIN | EN | AISI |
| 20MOCR4 | 763 | 1.7321 | 20MoCr4 | 20MoCr4KD | 8620 |
Composição quimica (em% em peso)
| C | Si | Mn | Cr | Mo | Ni | V | W | Outros |
| 0.20 | máx. 0.40 | 0.85 | 0.45 | 0.45 | - | - | - | - |
Descrição
One of the most popular and widely used carborizing steels available. 20MoCr4 is a hardenable chromium, molybdenum, nickel low alloy steel often used for carburizing to develop a case-hardened part. This case-hardening will result in good wear characteristics.
Aplicações
Gears, shafts and other applications where a hard carborized case and a tough core are desired.
Propriedades físicas (valores médios) à temperatura ambiente
Módulo de elasticidade [103 x N / mm2]: 210
Densidade [g / cm3]: 7.85
Coeficiente de Expansão Térmica Linear 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC |
| 11.1 | 12.1 | 12.7 | 12.9 | 13.5 |
Recozimento macio
Aquecer para 650-700oC, esfrie lentamente. Isso produzirá uma dureza Brinell máxima de 207.
Tratamento térmico
| Anti-germes | Temperatura | Resfriamento |
| Case hardening | 880-980oC | Oil (water), hot bath 160-250oC |
| Carburising | 880-980oC | Oil (water), hot bath 160-250oC |
| Direct hardening | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 780-820oC | Oil, hot bath 160-250oC |
| Temperamento | 150-200oC | ar |
Forjar
Temperatura de conformação a quente: 1050-850oC.
Usinabilidade
Machining is done prior to carburizing to within as close a tolerance as possible. Finish machining, after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment – after carburizing machining is usually limited to grinding.
Soldagem
The alloy may be welded by conventional methods, usually gas or arc welding. Preheating at 200oC is beneficial and subsequent heating after welding is recommended – consult the approved weld procedure for the method used.
Trabalho a frio
The alloy may be cold worked in the annealed condition by conventional methods. Cold working, as with machining, should be done to as close a tolerance as possible before heat treatment or carburizing.
Formulários fabricados: consulte o Programa de vendas dimensionais.
Aviso Legal
As informações e dados aqui apresentados são valores típicos ou médios e não garantem valores máximos ou mínimos. Os aplicativos especificamente sugeridos para o material aqui descrito são feitos apenas com o objetivo de ilustração, para permitir que o leitor faça sua própria avaliação e não se destinam a garantias, expressas ou implícitas, de adequação a esses ou outros objetivos. Não há representação de que o destinatário desta literatura receberá edições atualizadas à medida que estiverem disponíveis.