Aço AISI 4140 / 1.7227 / 42CrMoS4
- Grade:
Clique Para Email do Vendedor
Partilhar este anúncio
Especificação, Chemical & desempenho mecânico
AISI 4140 Steel Bar, Steel Plate, Flats Supplier, Stockist and Exporter. AISI SAE 4140 alloy steel is a chromium molybdenum alloy steel specification widely used in general purpose high tensile steel for components, like axles, shafts, bolts, gears and other applications. Similar to alloy grade AISI 4130 chrome moly alloy steel but with a slightly higher carbon content. The higher carbon content of AISI 4140 steel gives greater strength and heat treatment capabilities in comparison to AISI / ASTM 4130 alloy steels, however it does have inferior weldability characteristics.
Podemos produzir 1.7227, DIN 42CrMoS4, AISI 4140 stainless steel round rods, 1.7227, DIN 42CrMoS4, AISI 4140 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong Group production experience, strict control 1.7227, DIN 42CrMoS4, AISI 4140 chemical composition and 1.7227, DIN 42CrMoS4, AISI 4140 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.
Supply Range for AISI alloy 4140 steel
Barra redonda de aço 4140: diâmetro 8mm - 3000mm
Placa de aço 4140: espessura 10mm - 1500mm x largura 200mm - 3000mm
4140 Steel Grade Square: 20mm – 500mm
Acabamento da superfície: preto, usinado em bruto, torneado ou conforme exigências.
Largura: 10mm para 2500mm
Lenth: Nós podemos fornecer qualquer lenth com base na exigência do cliente.
Designação por normas
| Marca | Ravne No. | Esteira. Não. | DIN | EN | AISI |
| 42CRMOS4 | 792 | 1.7227 | 42CrMoS4 | 42CrMoS4 | 4140 |
Composição quimica (em% em peso)
| C | Si | Mn | Cr | Mo | Ni | V | W | Outros |
| 0.41 | máx. 0.40 | 0.75 | 1.05 | 0.28 | - | - | - | - |
Descrição
Aço estrutural especial.
Aplicações
High and moderately stressed components for automobile industry and mechanical engineering – shafts, connecting rods, crankshafts, screws, etc.
Propriedades físicas (valores médios) à temperatura ambiente
Módulo de elasticidade [103 x N / mm2]: 210
Densidade [g / cm3]: 7.80
Recozimento macio
Aquecer para 680-720oC, resfrie lentamente no forno. Isso produzirá uma dureza Brinell máxima de 241.
Normalizando
Temperatura: 840-880oC.
Endurecimento
Endurecer de uma temperatura de 820-860oC followed by oil or water quenching.
Temperamento
Temperatura de têmpera: 540-680oC.
Mechanical Properties in Quenched and Tempered Condition
| Diâmetro (mm) | 0.2 proof stress (N/mm2) | Tensile stregth (N/mm2) | Alongamento (%) | Reduction (%) | Impact energy (J) |
| Até 16 | 900 | 1100-1300 | 10 | 40 | 30 |
| 17-40 | 750 | 1000-1200 | 11 | 45 | 35 |
| 41-100 | 650 | 900-1100 | 12 | 50 | 35 |
| 101-160 | 550 | 800-950 | 13 | 50 | 35 |
| 161-250 | 500 | 750-900 | 14 | 55 | 35 |
Endurecibilidade no teste de têmpera final
Quenching temperature in the end-quench test is 850oC
| Dureza | 1.5 | 3 | 5 | 7 | 9 | 11 | 13 | 15 | 20 | 25 | 30 | 35 | 40 | 45 | 50 |
| H máx. | 61 | 61 | 61 | 60 | 60 | 59 | 59 | 58 | 56 | 53 | 51 | 48 | 47 | 46 | 45 |
| H min. | 53 | 53 | 52 | 51 | 49 | 43 | 40 | 37 | 34 | 32 | 31 | 30 | 30 | 29 | 29 |
| HH máx. | 61 | 61 | 61 | 60 | 60 | 59 | 59 | 58 | 56 | 53 | 51 | 48 | 47 | 46 | 45 |
| HH min. | 56 | 56 | 55 | 54 | 52 | 48 | 46 | 44 | 41 | 39 | 38 | 36 | 36 | 35 | 34 |
| HL máx. | 58 | 58 | 58 | 57 | 56 | 54 | 53 | 51 | 49 | 46 | 44 | 42 | 41 | 40 | 40 |
| HL min. | 53 | 53 | 52 | 51 | 49 | 43 | 40 | 37 | 34 | 32 | 31 | 30 | 30 | 29 | 29 |
Forjar
Temperatura de conformação a quente: 1050-850oC.