Aço de ferramenta ASTM T4 / 1.3255 / S 18-1-2-5 / SKH3

AISI T4 tool steel is one of tungsten type high speed tool steel, which belongs to ASTM A600 specification, the standard for high speed tool steel materials.

Aço para ferramentas ASTM T4 is similar to T1 Tool Steel materials, but with 4.25~5.75% cobalt added to increase heat resistance. The red hardness of T4 steel and the high temperature hardness is a little higher than T1 tool steel. AISI T4 tool steel is a deep hardening alloy capable of Rockwell C 64 hardness.

Otai Steel is one of the leading supplier of AISI/ASTM T4 tool steel high speed materials. We know the features of T4 high speed steel materials and different applications & your various applications. You have the T4 tool steel materials data below.

1.ASTM/AISI T4 Tool Steel Supply Range

Barra redonda T4 em aço: diâmetro 2mm - 200mm
Aços T4 Planos: espessura 2-20mm x largura 10-100mm
Placa de aço T4: espessura 2-200mm x largura 200-810mm
Acabamento da superfície: preto, usinado em bruto, torneado ou conforme exigências.

2.Relevant Steel Specifications of AISI T4 High Speed Tool Steels

País	EUA	German	Japão
Padrão	ASTM A600	ISO 4957	JIS G4403
Notas	T4 / T12004	S 18-1-2-5/1.3255	SKH3

3.AISI T4 Tool Steel and Equivalents’ Chemical Composition

ASTM A600	C		Mn		P	S	Si		Cr		V		W		Mo		Co
T4	0.70	0.80	0.10	0.40	0.03	0.03	0.20	0.40	3.75	4.50	0.80	1.20	17.50	19.00	0.40	1.00	4.25	5.75
DIN ISO 4957	C		Mn		P	S	Si		Cr		V		W		Mo		Co
S 18-1-2-5/1.3255	0.75	0.83	...	0.40	0.03	0.03	...	0.45	3.80	4.50	0.80	1.20	17.50	18.50	0.50	0.80	4.50	5.50
JIS G4403	C		Mn		P	S	Si		Cr		V		W		Mo		Co
SKH3	0.73	0.83	...	0.40	0.03	0.03	...	0.45	3.80	4.50	0.80	1.20	17.00	19.00	...	...	4.50	5.50

4.High Speed Steel T4 Tool Steel Mechanical Properties

• Propriedades físicas dos aços para ferramentas T4 de alta velocidade
  • Physical properties (average values) at ambient temperature
  • Modulus of elasticity [103 x N/mm2]: 217
  • Density [g/cm3]: 8.70
  • Condutividade térmica [W / mK]: 19.0
  • Electric resistivity [Ohm mm2/m]: 0.65
  • Capacidade térmica específica [J / gK]: 0.46

• Mechanical Properties of T-4 Steel

Propriedades	métrico	imperial
Módulos de elasticidade	190-210 GPa	27557-30458 ksi
Relação de Poisson	0.27-0.30	0.27-0.30

• Thermal Properties of T4 Tool Steels

Propriedades	métrico	imperial
Thermal expansion co-efficient	11.9 µm/m°C	6.6 µin/in°F

Forjamento de materiais de aço para ferramentas ASTM T5

Forging of T4 steel can be carried out from 850 to 1120°C (1775 to 2100°F).

• Preheat T4 steel material uniformly and slowly to 860-880°C.
• Increase the forging temperature up to 1050-1120°C.
• T4 hss tool steel should be cooled very slowly after forging.

6.AISI/ASTM T4 Tool Steel Heat Treatment and Properties

• Endurecimento

Harden T4 high speed tool steel from a temperature of 1260-1290oC followed by oil, air quenching or warm bath at 550oC. Hardness after quenching is 63-66 HRC.

• recozimento

T4 steel should be annealed after hot working. Increase the temperature of T4 high speed steel to 860°C(Max220°C per hour). Hold at the temperature and then cool slowly with the furnace. The annealed hardness achieved should be below HB255.

• Temperamento

Tempering temperature: 2x 560-580oC. Hardness after tempering is 64-65 HRC.

7.Aplicações do aço para ferramentas ASTM / AISI T4

AISI T4 high speed tool steels are widely used as cutting tools, broaches and cold extrusion punches, turning, planing and milling cutters for roughing work.

Aplicações típicas são:

• Treinos,
• Fresas,
• Ferramentas de corte de linha,
• Ferramentas serrilhadas,
• Punções a extrusão a frio
• Broches etc.

Besides of ASTM/AISI T4 high speed tool steel materials, we are also capable of supplying T1 high speed steel, T10 tool steels, T15 tool steel etc. Just contact us for more details and latest price offer. If you have any questions, also leave a comment below.