800H, 800T, N08810, N08811, Incoloy Liga 800H, 1.4876
- Grade:
Clique Para Email do Vendedor
Partilhar este anúncio
Especificação, Chemical & desempenho mecânico
Ligas resistentes ao calor
800H / 800T (UNS N08810 / N08811), comparable to Incoloy 800H Alloy
800H, UNS N08810 / NAS 800T (UNS N08811) are nickel-iron-chromium alloys that provide high strength and excellent resistance to oxidation and carburization at high temperatures. High creep strength is attained through control over crystal grains—via high temperature heat treatment, together with fine control over carbon, titanium, and aluminum content.
Provide forms as following,
Trabalhabilidade
Whether for hot working or cold working, 800H/800T offer workability similar to austenitic stainless steels. For hot working, temperatures should be between 1000 and 1230℃, although light work may be done at temperatures as low as 850℃. To prevent cracks, we recommend avoiding the temperature range between 650 and 800℃. Although cold workability is similar to austenitic stainless steels, work hardening tends to be slightly lower.
soldabilidade
As with standard austenitic stainless steels, 800H/800T may be welded using techniques such as TIG, MIG, and shield metal arc welding. AWS ERNiCr-3/AWS ENiCrFe-2 welding rods are often used.
Tratamento térmico
800H/800T exhibit an austenite structure similar to austenitic stainless steels, and appropriate heat treatment procedures and requirements are similar. Typical heat treatments are as follows:
- Solution treatment: 1100~1170℃; rapid cooling
For applications requiring creep rupture strength in high-temperature environments, the following ASTM B409 heat treatment may be used:
Solution treatment:
- 1121℃ minimum (UNS N08810)
- 1149℃ minimum (UNS N08811)
Properties at High Temperatures
Because of its high nickel and chromium content, 800H/800T resist oxidation and carburization at high temperatures. 800H/800T are superior to Type 310S and approach 600 alloy in resistance to oxidation. Offering superior high-temperature strength nearly equal to N06600, 800H/800T are widely used in applications requiring heat resistance, as they do not become brittle due to sigma phase precipitation during use. While 800 alloy is generally used at temperatures below 600℃, 800H/800T are recommended for applications requiring superior creep properties at higher temperatures.
Resistência à Corrosão
800H/800T offer superior corrosion resistance in oxidizing corrosive environments such as nitric acid or nitric acid-sulfuric acid. Likewise, they perform well in sodium salt and other molten salt environments, with stress corrosion cracking resistance surpassing standard austenitic stainless steels.
Aplicações
800H/800T are widely used in chemical plants, heat treatment furnaces and other high-temperature environments.