NM15M Liga não magnética 17Cr-15Mn-4Ni-0.3N

Descrição breve

Um aço inoxidável austenítico de alto manganês, composto de 17Cr-15Mn-4Ni. Fornecendo maior resistência que os aços inoxidáveis ​​austeníticos não magnéticos convencionais, ele não magnetiza, mesmo que o frio trabalhe com força. Pode ser fornecido em formas de chapa, folha e tira.

The hot and cold workability of non-magnetic alloy is basically the same as that of standard austenitic stainless steels such as Type 304, Type 316, etc. However, the fact that this is a high strength material must be considered in both cold and hot working.

The heat treatment is similar to austenitic stainless steels. The typical heat treatment is as follows:Solution heat treatment: 1050~1150℃; rapid cooling

Non-magnetic springs, gaskets, electronic components, and other components where magnetism is not desired

Even when cold working is applied, there is no variation in the relative permeability,and it does not become magnetized.

After cold-rolling, the hardness can be raised to between 50 and70 Hv with heat treatment between 300 and 500°C.

Just as with the standard austenitic stainless steel Type 304, the corrosion resistance shows no degradation even after strong cold working.

Test condition: 5% NaCl, 30°C

Solution-treated 0.34V

60% cold-rolled No rusting