T1 Инструмент Stee / Высокая скорость / 1.3355 / HS18-0-1 / SKH2

AISI/ASTM T1 tool steel is one of the original tungsten high speed steels, although all tungsten steel grades are used to a limited extent because of the cost and questionable availability of tungsten. Of the T group steels, the general purpose T1 tool steels and the high-vanadium-cobalt T15 are most commonly used.

T1 high speed steel is an air or oil hardening tool steel which has good comprehensive performance. HSS T1 tool steel has a high hardness (HRC62~66), strength, toughness and heat resistance, which is an excellent cutting tool material. T-1 tool steel grade is on the whole used for turning, planning & slotting instruments, tapes, twist drill, threading dies, profile slicing instruments, broaching instruments & reamers.

Generally, high speed steels are divided into three groups:

• Those bearing the symbol T where tungsten is the major alloying element;
• Those bearing the symbol M indicating that molybdenum are the principal alloying element;
• A group of more highly alloyed steels that is capable of attaining unusually high hardness values.

Here we have tool steel type T-1 with the chemical composition, physical, mechanical and thermal properties and other equivalents of T1 tool steels. Except T1 hss tool steel, we are also able to supply T2, T10, T-15 high speed steel etc.

1.High Speed T1 Tool Steel Supply Range

T1 Steel Round Bar: diameter 2mm – 200mm

T1 Steel Flat: thickness 2-20mm x width 10-100mm

T1 Steel Plate: thickness 2-200mm x width 200-610mm

Поверхностная обработка: черная, с грубой обработкой, точеная или в соответствии с заданными требованиями.

2.Relevant Steel Specification of AISI T1 High Speed Tool Steels

Страна	США	German	Япония
Стандарт	ASTM A600	ISO 4957	JIS G4403
Оценки	T1	HS18-0-1/1.3355	SKH2

3.AISI T1 Tool Steel and Equivalents’ Chemical Composition Properties

ASTM A600	C		Mn		P	S	Si		Cr		V		Mo		W		Co
T1	0.62	0.80	0.10	0.40	0.03	0.03	0.20	0.40	3.75	4.50	0.90	1.30	...	...	17.25	18.75	...	...
ISO 4957	C		Mn		P	S	Si		Cr		V		Mo		W		Co
HS18-0-1/1.3355	0.73	0.85	...	...	...	...	...	0.65	3.60	4.50	1.00	1.20	...	...	17.20	18.70	...	...
JIS G4403	C		Mn		P	S	Si		Cr		V		Mo		W		Co
SKH2	0.73	0.83	...	0.40	0.03	0.03	...	0.45	3.80	4.50	1.00	1.20	...	...	17.20	18.70	...	...

4.High Speed Steel T1 Tool Steel Mechanical Properties

• Physical Properties of HSS T-1 Steels

Недвижимость	Метрика	императорский
Плотность	8.67 г / cm3	0.313 lb/in3

• Mechanical Properties of T-1 Steel

Недвижимость	Метрика	императорский
Hardness, Rockwell C	63.0 - 65.0	63.0 - 65.0
Коэффициент Пуассона	0.27-0.30	0.27-0.30
Модуль упругости	190-210 ГПа	27557-30457 KSI

• Thermal Properties of T1 Tool Steel

Недвижимость		условия
		Т (° С)	Лечение
Термическое расширение	9.7 x 10-6 / ºC	20-200 more	-
Теплопроводность	19.9 x W/m-K	100 более	-

5.Forging of AISI HSS T1 Tool Steel

1. Preheat T1 high speed steel uniformly and slowly to 850-880°C.
2. Increase the forging temperature for T-1 tool steel until 1050-1130°C.
3. T1 hss tool steel should be cooled very slowly after forging.

6.AISI/ASTM T1 Tool Steel Heat Treatment and Properties

Лечение	Диапазон температур	Cooling/Quenching	Примечания
Ковка	1700-2100° F	Медленный.	Cool slowly in dry sand or in other insulating media.
отжиг	1600-1650° F	Cool slowly at a rate of 35° F per hour to 1000° F.	For best results, insulating media is desirable. Hold at temperature for 2 hours.
Снятие напряжения	1100-1300° F	Cool slowly	Stress relieve after rough machining
подогрев	1500-1550° F		Preheat time in furnace is ¾ Hr. per inch of thickness. Heating up to temperature as slow as possible.
упрочнение	2325-2375° F (furnace)	Quench in air or warm oil. To minimize quenching strains, quench in salt at 1000° F	For maximum wear resistance, harden at 2375° F. For maximum toughness and high hardness, harden at 2275° F.
	2275-2350° F (salt bath)
закал	1022 ° F-1058 ° F	Temper T1 high-speed steel immediately after quenching. Hold for at least two hours	Double tempering is recommended. The usual tempering time is 2+2 hours. Recommended temperature is 1000-1075° F for cutting tools. 1100-1200° F for shock tools

7.Applications of ASTM/AISI T1 Tool Steel

Generally, high speed steels are used for machining at high speeds. HSS T1 steel materials are widely used for:

• Развертки
• Сверла
• Hobs
• Knurling Tools
• Lathe Tools
• Milling Cutters
• Nut Piercers
• Planer Tools
• Развертки
• Shaving Tools
• Отводы
• Thread Cutting Tools

We are capable of supply top quality T1 tool steel high speed also in good price, you could send us enquiries of T1 steel and request the latest offer. And leave a comment if there are any queries.