Especificación, química y rendimiento mecánico
Designación por normas
| XNUMX- Cuales serian las circunstancias por las cuales tu producto cambiaria de precio? (Obligatorio - Publico) | Ravne No. | Estera. No. | DIN | EN | AISI |
| 20MOCR4 | 763 | 1.7321 | 20MoCr4 | 20MoCr4KD | 8620 |
Composición química (en% en peso)
| C | Si | Mn | Cr | Mo | Ni | V | W | Otros |
| 0.20 | máx. 0.40 | 0.85 | 0.45 | 0.45 | - | - | - | - |
Descripción
One of the most popular and widely used carborizing steels available. 20MoCr4 is a hardenable chromium, molybdenum, nickel low alloy steel often used for carburizing to develop a case-hardened part. This case-hardening will result in good wear characteristics.
Aplicaciones
Engranajes, ejes y otras aplicaciones en las que se desea una carcasa dura carborizada y un núcleo resistente.
Propiedades físicas (valores promedio) a temperatura ambiente
Módulo de elasticidad [103 x N / mm2]: 210
Densidad [g / cm3]: 7.85
Coeficiente de expansión térmica lineal 10-6oC-1
| 20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC |
| 11.1 | 12.1 | 12.7 | 12.9 | 13.5 |
Recocido suave
Calentar a 650-700oC, enfriar lentamente. Esto producirá una dureza Brinell máxima de 207.
Tratamiento térmico
| Tratamiento | Temperatura | Enfriamiento |
| Case hardening | 880-980oC | Oil (water), hot bath 160-250oC |
| Carburising | 880-980oC | Oil (water), hot bath 160-250oC |
| Direct hardening | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 860-900oC | Oil, hot bath 160-250oC |
| Core refining | 780-820oC | Oil, hot bath 160-250oC |
| Temperamento | 150-200oC | Air |
Forjando
Temperatura de formación en caliente: 1050-850oC.
maquinabilidad
Machining is done prior to carburizing to within as close a tolerance as possible. Finish machining, after heat treatment and/or carburizing, should be at a minimum so as not to impair the hardened case of the part. Machining may be done by conventional means prior to heat treatment – after carburizing machining is usually limited to grinding.
Soldadura
The alloy may be welded by conventional methods, usually gas or arc welding. Preheating at 200oC is beneficial and subsequent heating after welding is recommended – consult the approved weld procedure for the method used.
Trabajo en frío
The alloy may be cold worked in the annealed condition by conventional methods. Cold working, as with machining, should be done to as close a tolerance as possible before heat treatment or carburizing.
Formularios fabricados: consulte el Programa de ventas dimensionales.
Términos y Condiciones
La información y los datos presentados aquí son valores típicos o promedio y no son garantía de valores máximos o mínimos. Las aplicaciones específicamente sugeridas para el material descrito en este documento se realizan únicamente con el propósito de ilustrar para permitir al lector hacer su propia evaluación y no tienen la intención de ser garantías, expresas o implícitas, de idoneidad para estas u otras pupilas. No hay representación de que el destinatario de esta literatura reciba ediciones actualizadas a medida que estén disponibles.