| Le formulaire |
ASTM |
| Tige, barre et forme |
UN 564, UN 484 |
| Plaque, feuille et bande |
UN 693, UN 480 |
| Forger |
UN 705, UN 484 |
Composition chimique
|
%
|
Ni
|
Cr
|
Mo
|
Fe
|
Co
|
W
|
C
|
Mn
|
Si
|
P
|
S
|
Al
|
Cu
|
La
|
B
|
|
min
|
équilibre
|
14.5
|
14.0
|
|
|
|
|
0.30
|
0.20
|
|
|
0.10
|
|
0.01
|
|
|
max
|
17.0
|
16.5
|
3.0
|
2.0
|
1.00
|
0.020
|
1.00
|
0.75
|
0.020
|
0.015
|
0.50
|
0.35
|
0.10
|
0.015
|
Propriétés physiques
| Densité |
7.75 g / cm3 |
| Gamme de fusion |
1404-1440 ℃ |
Caractéristiques: 17-4PH is a chromium-nickel-copper precipitation hardening martensitic stainless steel that combines oxidation and corrosion resistance comparable to 304 in most environments with high strength and hardness. It is the most widely used of all the precipitation hardening stainless steels, and is more cost effective than many high nickel non-ferrous alloys in some
Applications. 17-4PH cannot be used at temperatures above 300℃ and at cryogenic temperatures. It is magnetic.
Industrie aérospatiale, outils à main biomédicaux, équipement de traitement chimique et alimentaire, traitement et stockage des déchets nucléaires, métallurgie générale et équipement de papeterie.