AISI 1020,1.0402, DIN C22,
- Grade:
Cliquez pour envoyer un courriel Vendeur
Partager cette annonce
Spécification, Chemical & Performance mécanique
We can produce 1.0402, DIN C22, Tiges rondes en acier inoxydable AISI 1020, 1.0402, DIN C22, AISI 1020 forging,sheet,coil,and profiledstrip,Deformed steel,flat steel,mould,steel wire,have all specifications. With Bozhong production experience, strict control 1.0402, DIN C22, AISI 1020 chemical composition and 1.0402, DIN C22, AISI 1020 mechanical properties.From casting, forging, steel to hot and cold rolling process, heat treatment, etc, we have the control of professional engineers. We have advanced precision machining equipment, according to the requirements of users machining. in order to achieve the most satisfied with the user requirements.
Spécification de production
Barre ronde en acier: 1mm à 3500mm
Acier carré: 1mm à 4000mm
Tôle d'acier:0.1mm à 4000mm
Largeur: 10mm à 2500mm
Lenth: Nous pouvons fournir toute lentille en fonction des besoins du client.
Forge: Arbres à flancs / tuyaux / tubes / limaces / beignets / cubes / autres formes
Tubes: OD: φ6-1800mm, avec une épaisseur de paroi allant de 1-35 mm.
Condition des produits finis: forgeage à chaud / laminage à chaud + recuit / normalisation + revenu / trempe + revenu / toutes conditions basées sur les exigences du client
Conditions de surface: à l'échelle (finition de travail à chaud) / rectifié / usinage grossier / usinage fin / en fonction des besoins du client
Fours de traitement métallurgique: arc d'électrode + électrode consommable LF / VD / VOD / ESR / Vide.
Inspection par ultrasons: 100% inspection par ultrasons pour toutes les imperfections ou en fonction des besoins du client Excellent service pour toutes sortes d'industries, avec des avantages des technologies, de l'équipement et du prix.
Nous sommes à votre service en toute honnêteté, intégrité et professionnalisme.
Désignation par normes
| Marque | LH No. | Tapis. Non. | DIN | EN | AISI |
| C22 | 514 | 1.0402 | C22 | - | 1020 |
Composition chimique (en% en poids)
| C | Si | Mn | Cr | Mo | Ni | V | W | Autres |
| 0.22 | max. 0.40 | 0.55 | max. 0.40 | max. 0.10 | max. 0.40 | - | - | (Cr + Mo + Ni) = max. 0.63 |
Description
C22 is one of the very commonly used plain carbon steels. It has a nominal carbon content of 0.22% with approximately 0.55% manganese. It is a good combination of strength and ductility and may be hardened or carburized.
Applications
C22 steel is used for simple structural application such as cold headed bolts. It is often used in the case hardened condition.
Propriétés physiques (valeurs moyennes) à température ambiante
Module d'élasticité [103 x N / mm2]: 210
Densité [g / cm3]: 7.70
Conductivité thermique [W / mK]: 51.9
Résistivité électrique [Ohm mm2/ m]: 0.11
Capacité thermique spécifique [J / gK]: 0.46
Recuit doux
Chauffer à 870-980oC, cool slowly. This will produce a minimum tensile strength of 450 Mpa.
Stress Soulager
La décompression pour éliminer les contraintes d'usinage doit être effectuée par chauffage à env. 540oC, maintien pendant 1-2 heures à chaud, suivi d'un refroidissement par air. Cette opération est réalisée pour réduire la distorsion lors du traitement thermique.
durcissement
Durcir à une température de 820-870oC suivi d'une trempe à l'eau.
Tempérer
Température de revenu: veuillez demander.
Forger
Température de formage à chaud: 1200-950oC.
Usinabilité
Machinability is good at 65% compared to 1112 carbon steel as 100% baseline.
Résistance à la corrosion
Not corrosion resistant. The steel will rust unless protected.
Soudage
Readily weldable by all of the standard methods.
Fonctionnement à froid
C22 steel is readily cold worked by all conventional methods. A stress relief anneal may be needed after extensive cold work.
Propriétés mécaniques