NM15M 비자 성 합금 17Cr-15Mn-4Ni-0.3N

간단한 설명

17Cr-15Mn-4Ni의 합성물 인 고 망간 오스테 나이트 계 스테인리스 강. 기존의 비자 성 오스테 나이트 계 스테인리스 강보다 강도가 높기 때문에 냉기가 힘을 가해도 자화되지 않습니다. 판, 시트 및 스트립 형태로 공급할 수 있습니다.

The hot and cold workability of non-magnetic alloy is basically the same as that of standard austenitic stainless steels such as Type 304, Type 316, etc. However, the fact that this is a high strength material must be considered in both cold and hot working.

The heat treatment is similar to austenitic stainless steels. The typical heat treatment is as follows:Solution heat treatment: 1050~1150℃; rapid cooling

Non-magnetic springs, gaskets, electronic components, and other components where magnetism is not desired

Even when cold working is applied, there is no variation in the relative permeability,and it does not become magnetized.

After cold-rolling, the hardness can be raised to between 50 and70 Hv with heat treatment between 300 and 500°C.

Just as with the standard austenitic stainless steel Type 304, the corrosion resistance shows no degradation even after strong cold working.

Test condition: 5% NaCl, 30°C

Solution-treated 0.34V

60% cold-rolled No rusting