Thép công cụ ASTM T5 / 1.3265 / S18-1-2-10 / SKH4 / BT5

Thép công cụ ASTM T5 is one of tungsten high-speed tool steel. It belongs to ASTM A600, together with T1, T2, T4 Tool Steel etc. They are also in T group in ASTM A600 standard. AISI T5 high speed steel contains Cobalt with range 7.0~9.5%. AISI T5 steel has better high temperature performance, toughness and better cutting performance than ASTM T4 steel. Similar to T4 steel materials, T5 tool steels are also used for cutting tool, turning tool etc.

1.ASTM T5 Tool Steel Supply Range

Thanh tròn thép T5: đường kính 2mm - 200mm
Thép T5 phẳng: độ dày 2-20mm x chiều rộng 10-100mm
Thép tấm T5: độ dày 2-200mm x chiều rộng 200-810mm
Bề mặt hoàn thiện: Đen, Gia công thô, Bóc vỏ, Quay hoặc theo yêu cầu nhất định.

2.Relevant Steel Specifications of AISI T5 Tool Steel

Quốc gia	Hoa Kỳ	Tiếng Đức	Nhật Bản	Anh
Tiêu chuẩn	ASTM A600	DIN EN ISO 4957	JIS G4403	BS 4659
các lớp	T5 / T12005	1.3265/S18-1-2-10	SKH4	BT5

3.AISI T5 Tool Steels and Equivalents’ Chemical Composition

ASTM A600	C		Mn		P	S	Si		Cr		V		W		Mo		Co
T5	0.75	0.85	0.20	0.40	0.03	0.03	0.20	0.40	3.75	5.00	1.80	2.40	17.50	19.00	0.50	1.25	7.00	9.50
DIN ISO 4957	C		Mn		P	S	Si		Cr		V		W		Mo		Co
1.3265/S18-1-2-10	0.72	0.80	...	0.40	0.03	0.03	...	0.45	3.80	4.50	1.40	1.70	17.50	18.50	0.50	0.80	9.00	10.00
JIS G4403	C		Mn		P	S	Si		Cr		V		W		Mo		Co
SKH4	0.73	0.83	...	0.40	0.03	0.03	...	0.45	3.80	4.50	1.00	1.50	17.00	19.00	...	...	9.00	11.00
BS 4659	C		Mn		P	S	Si		Cr		V		W		Mo		Co
BT5	0.75	0.85	...	0.40	0.35	0.35	...	0.40	3.75	4.50	1.75	2.05	18.50	19.50	...	1.00	9.00	10.00

4.High Speed Tool Steel T5 Mechanical Properties

• Tính chất vật lý của thép công cụ T5 tốc độ cao

Bất động sản	Tỉ trọng kg/dm3	Temperature T °C/F	Specific heat J / kgK	dẫn nhiệt W/mK	Electric resistance µΩ·cm	Mô đun đàn hồi kN/mm2	Nhiệt độ. °C/°F	Creep strain limit (10000h) (Rp1,0) N/mm2	Creep rupture strength (10000h) (Rp1,0) N/mm2
445 (≥)	839 (≥)	42	42	34	Giải pháp và Lão hóa, Ủng hộ, Sức khỏe, Q + T, v.v.	424	883	167	975

• Mechanical Properties of HSS T-5 Steel

Bất động sản	metric	hoàng đế
Tỉ trọng	8.75 g / cm3	0.316 lb/in3
Bất động sản	metric	hoàng đế
Tỷ lệ của Poisson	0.27-0.30	0.27-0.30
Mô đun đàn hồi	GPUMX-190 GPa	27557-30458 ksi

5.Forging của vật liệu thép công cụ ASTM T5

Hot forming temperature: 1150-900oC.

6.ASTM T5 Tool Steel Heat Treatment

• Annealing of T-5 Steel
  • Annealing is recommended after hot working and before re hardening
  • Heat the temperature to 850°C at a rate of no more than 220°C per hour.
  • Hold at the temperature for one hour per inch of thickness(at least two hours).
  • Cool slowly in the furnace or in air to ambient temperature.
  • The resultant hardness achieved should be Max 255HB or lower.

• Giảm stress

Stress relieving to remove machining stresses should be carried out by heating to 600-650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.

• Hardening of Steel T5
  • Preheat T5 tool steel slowly to the temperature of 820-870°C.
  • Heat to the final hardening temperature of 1250°C and make sure the material must be heated through.
  • Quench in the warm oil,and then complete the quench in air.(care must be taken at this step)
• Tempering of T-5 Steel

Tempering temperature: 550-590oC.

Nhiệt độ ủ (^oC) so với độ cứng (HRC)

100oC	150oC	200oC	250oC	300oC	350oC	400oC	450oC	500oC	550oC	600oC	650oC
64	64.5	63	62.5	62	62	62.5	63.6	64.8	66	64	60

7.Ứng dụng của thép công cụ ASTM / AISI T5

ASTM T5 high speed steels are generally used as cutting tools, broaches and cold extrusion punches, turning blades, punchers, metal working blades.

Các ứng dụng điển hình là:

• Mũi khoan,
• Dao phay,
• Công cụ cắt ren,
• Dụng cụ gõ nút,
• Đấm lạnh
• Broaches, vv

Besides AISI T5 high speed tool steel, we could also supply you T1, T2, T4, T10, T15 tool steel. Just send us your requests and have our best T5 tool steel price and other HSS tool steel offer.